PVC paste resin for conveying belt, tarpaulin)

1.PVC paste resin CAN1253 2.low viscosity 3.partical size 0.5-2microm 4.similar with LG PB1302, P440 5. for spread coating

PVC Paste resin, emulsion grade.

Synonyms: Emulsion Polyvinyl Chloride resin, chloroethylene polymer paste, chloroethylene homopolymer paste, PPVC, EPVC, PVC resin paste grade, PVC resin emulsion grade, Paste PVC resin emulsion grade

Characteristic: Paste PVC is a homopolymer of PVC which is made by emulsion polymerization, It has incombustible feature and can be used for coating cloth, rotary forming, macerating, spraying and foaming after mixed with plasticizer and other addition agent. It has a light white and micro powder.

Application:

This product is a high-quality raw material in producing foam floor, wall paper, leathererette, soft and hard foam plastic for sound insulation and heat insulation, toy, glove,paperboard coat, conveying belt, fitting of car, adhesive and seal gum for car coated glass and so on.

Specifications:

SPECS		CAN1702	CAN1552	CAN1401	CAN1402	CAN1253	CAN1104	CAN0954
Viscosity (Ml/G)		155-165	155-145	140-150	130-140	115-135	100-120	85-105
K Value		75.0-79.0	75.0-79.0	73.5-76.0	71.5-73.5	67.5-72.5	63.5-69.0	59.0-65.0
Polymerization Degree		1750-1950	1550-1750	1475-1650	1300-1475	1100-1350	900-1150	720-950
B-type Viscosity 30°C mpa.s		3.0-5.0	5.0-7.0	4.0-7.0	6.0-8.0	6.0-10.0	9.0-11.0	11.0-13.0
Impurity Number		12	12	12	20	20	20	40
Volatile % ≤		0.4	0.4	0.4	0.5	0.5	0.5	0.5
Bulk density, g/cm3		0.3-0.45
Remain % mg/kg	0.25mm Sieve ≤	0.01	0.01	0.01	0.1	0.1	0.2	0.2
	0.063mm Sieve ≤	0.1	0.1	0.1	1	1	1	3
DOP: resin (portion)		100:100	60:100	100:100	60:100	100:100	60:100	100:100
Scraping size,μm ≤		100	100	100	___	___	___	___
VCM residue mg/kg		5	5	5	10	10	10	10

Package:

25kg/20kg PP woven bag or paper bag with inner lined plastic film, 13.5 MT / 20 FCL .

Storage and transport:

Prevent from rain, snow, humid, sunshine, throwing and other mechanical damage.

PVC paste resin for conveying belt, tarpaulin)